V-REFLEX ^™ Reflective Material–High Gloss Reflective Tape are designed for use on safety garments and when properly used, help enhance the visibility of the wearer in nighttime or low-light conditions when illuminated by headlights. 

V-REFLEX ^™ Reflective Material–High Gloss reflective Tape consist of highly retroreflective microprisms formed on flexible, glossy and UV-stabilized polymeric film. A flexible vinyl film sealed on the backside of the reflective sheeting encapsulates the microprisms and protects the reflective product from dirt and moisture penetration.

Test each application according to appropriate care instructions required for the finished product. Actual life of V-REFLEX ^™ reflective material high gloss products depends on cleaning methods and wear conditions. 

V-REFLEX^TM Reflective Material - Retro-Reflective Fabric/Tape meets or exceeds the following specifications as noted. All R_A values are over 100 cd/lux/m2 measured at +5.0° entrance angle and 0.2° observation angle after tests are carried out according to following test method

Retro-reflectivity (initial): ANSI/ISEA 107-2010 level 2 , EN ISO 20471

OEKO-TEX 100: Product Class II

Abrasion: 5000 cycles (EN 530 Method 2) | R_A  > 100 

Flexing: 7500 cycles (ISO 7854 Method A) | R_A  > 100 

Cold Fold: -20° (ISO 4675) | R_A > 100 

Temperature Variation: 50 hours @ 50 °C and 20 hours @ -30 °C | R_A  > 100 

Dry-Cleaning:  N/A

Wet Reflectivity: ANSI/ISEA 107-2010, EN ISO 20471 | R_A  > 100

Flame Resistant and Fire Retardant: 

• EN ISO 14116:2008; EN ISO 11611:2015; EN ISO 11612:2015;
• NFPA 1971:2013; NFPA 1977:2016; NFPA 2112:2012

Whenever two or more pieces of V-REFLEX ^™ reflective material are used together on a single surface or as a set, they should be matched to ensure uniform color and reflectivity. All safety garments should be constructed in accordance with ANSI/ISEA 107 or other prevailing standard.

Sewing to Fabrics: Sew in place with no more than 8 stitches per inch (2.54 cm), and not less than 1/8" (3 mm) from the edge of the material. Thread recommendation: 100% polyester. To reduce sticking, apply a non-stick material (e.g., silicone or nylon) to the bottom of the presser foot. Sewing channels along the edge are provided on High Gloss reflective Tape  to protect against water penetration. Sew down the center of the 1/4" wide sewing channels.

Welding to Fabrics: V-REFLEX ^™ Reflective Material–High Gloss reflective Tape are composed primarily of vinyl materials and will weld suitably to most PVC films with any of the following methods: radio frequency (RF), high frequency (HF), dielectric or ultrasonic. Adhesion to specific films will vary with the lubricants, pigments, plasticizers and fillers used to make the PVC film. It is important to test weld strength with each new lot and new vendor.

RF Sealing: Radio Frequency is a widely used method of sealing vinyl films. It has the advantage of handling patches and tapes using a step-and repeat process.

Screen Printing: All inks should be continuously tested to ensure acceptable adhesion in the event of changes occurring in the manufacturing process or composition of the ink. Prior to printing, wiping the surface with a soft cloth lightly dampened with alcohol may help prevent ink adhesion failure.